# Green Hydrogen Without Platinum and Ruthenium: Scientists Assemble Cheap Catalysts Using Nickel, Iron, and MXene

![Laboratory water electrolysis setup with electrodes and microscopic structure of the MXene-based catalyst.](https://xab.info/media/2026/10/28/zeleny-vodorod-deshovye-katalizatory-na-mxene/zeleny-vodorod-deshovye-katalizatory-na-mxene-1.webp)

## Key Points

- New catalysts based on nickel and iron oxides anchored on carbon nanofibers over an MXene (Ti3C2Tx) substrate are proposed as a replacement for expensive ruthenium and platinum.
- In alkaline electrolysis, the nickel composite exceeded the voltage of the reference RuO2 by only 50 mV in the oxygen evolution reaction.
- In assembled electrolyzer prototypes at 10 mA/cm², the iron cell showed 2.2 V and the nickel cell showed 2.7 V; 24-hour tests revealed only minor degradation.
- The work was published in ACS Applied Nano Materials; the authors note that research is ongoing.

The production of "green" hydrogen — a fuel obtained through water electrolysis powered by solar and wind energy — has long hit an economic wall: catalysts. Water-splitting reactions require expensive noble and rare metals such as platinum, ruthenium, and iridium, and it is their cost that makes clean hydrogen uncompetitive against fossil fuels. In a recent paper published in the journal ACS Applied Nano Materials, researchers demonstrated that this obstacle can be bypassed by anchoring active sites onto iron and nickel supported by carbon nanofibers grown on a two-dimensional conductive MXene material.

### The Problem Keeping Hydrogen Expensive

An electrolyzer simultaneously runs two reactions: hydrogen evolution at one electrode and oxygen evolution at the other. Both are critical to the process, and both are traditionally accelerated by catalysts based on ruthenium oxide (RuO2) and related compounds. Ruthenium, iridium, and platinum are rare metals with volatile prices, and their share in the installation's cost can be comparable to the price of the electronics themselves. Replacing them with industrially accessible iron and nickel fundamentally changes the economics of green hydrogen — provided the new materials maintain acceptable electrochemical activity.

### Architecture of the New Material: MXene, Nanofibers, and Metal Oxides

The foundation of the proposed catalysts is a two-dimensional MXene material with the composition Ti3C2Tx, known for its high electrical conductivity. Using chemical vapor deposition (CVD), the scientists grew carbon nanofibers on its surface, with nickel or iron oxide particles forming at their tips. Microscopy and spectroscopy confirmed that the fibers indeed formed and the layered structure of the MXene was preserved. The nickel composite turned out to be structurally more ordered: its carbon phase resembled graphite and contained fewer defects than the iron analog, which, according to the authors, explains some of the differences in electrochemical behavior.

### Testing Figures: How Close to Ruthenium

In alkaline water electrolysis, ruthenium oxide serves as the benchmark reference, requiring an overpotential of about 250 mV for the oxygen evolution reaction. The MXene-supported nickel composite required only 50 mV more for the same reaction, while the iron composite required 360 mV more. For the hydrogen evolution reaction, the gaps were larger: nickel needed +490 mV over the reference to achieve a current density of 10 mA/cm², and iron needed +520 mV. Thus, the nickel material came closest to ruthenium specifically in the oxygen reaction, while the difference in raw metal cost between nickel and ruthenium is incomparably larger than these tens of millivolts. The authors emphasize that anchoring the nanofibers onto MXene improved the performance of both composites compared to similar materials without such a substrate.

### Assembled Electrolyzers and 24-Hour Stability

The researchers went beyond laboratory electrodes and assembled prototype electrolyzers using the same type of catalyst on both electrodes. At a current density of 10 mA/cm², the iron cell showed a voltage of 2.2 V, and the nickel cell showed 2.7 V. Here the picture inverts: at the level of individual composites, nickel looked stronger, but in the fully assembled construction, iron yielded a better result. The authors suggest that iron stabilizes the environment during the reactions. 24-hour tests revealed a slight decrease in activity and characteristic drift in both materials, with the nickel catalyst degrading less. The authors explicitly state that the work is not finished, but the results are encouraging.

### Why This Matters for Energy

Green hydrogen is one of the few ways to obtain fuel without carbon dioxide emissions if the electrolysis energy comes from the sun and wind. As long as catalysts remain expensive, clean hydrogen loses on price even with a carbon tax, and industry scaling is held back. Transitioning to iron and nickel with an MXene substrate reduces this cost gap and paves the way for cheaper electrolyzers. Questions of long-term stability and scaling the CVD process to industrial areas remain, but the core principle — replacing a rare metal with an accessible one while maintaining activity via nanostructure — has already been experimentally confirmed.

## Fact-Check & Sources

- [Зелёный водород за недорого: учёные нашли альтернативу катализаторам из рутения window-new](https://3dnews.ru/1150543/zelyoniy-vodorod-za-nedorogo-uchyonie-nashli-alternativu-katalizatoram-iz-ruteniya) - Primary source: MXene composition Ti3C2Tx, CVD method, overpotential figures (50/300/360/490/520 mV), cell voltages of 2.2 and 2.7 V at 10 mA/cm², 24-hour test results.
- [Материал на основе серы позволяет получать зелёный водород из воды под действием света](https://www.elec.ru/news/2026/10/06/material-na-osnove-sery-pozvoljaet-poluchat-zelyon.html) - Relates to a different study (sulfur materials, Oregon State University) and does not overlap with the primary facts; used only as context for green hydrogen, not included in the text.

## FAQ

### What is MXene and why is it needed in the new catalyst?

MXene (composition Ti3C2Tx in the study) is a two-dimensional conductive material with high electrical conductivity. It serves as a substrate on which carbon nanofibers with nickel or iron oxide particles at the tips are grown via CVD.

### How close is the new nickel catalyst to the reference ruthenium oxide?

In the oxygen evolution reaction during alkaline electrolysis, the nickel composite required an overpotential of only 50 mV compared to RuO2, which requires about 250 mV.

### Which material — nickel or iron — showed a better result in the assembled electrolyzer?

In the fully assembled cell at a current density of 10 mA/cm², the iron composite yielded 2.2 V and the nickel composite yielded 2.7 V, meaning iron proved more effective in the finished design, although at the individual composite level nickel looked stronger.

### How stable are the new catalysts?

24-hour tests showed a minor decrease in activity and characteristic drift; the nickel catalyst changed less than the iron one. The authors point out that the work is not yet complete.